Lantor Soric XF
■The cost effective solution for closed mould processes
■ Is used as core material and infusion medium
■ Is a pressure stable polyester nonwoven and compatible with all regular types of resins,including Polyester,
Vinylester,Phenolic and Epoxy
■ Is suitable for closed mould processes,includingInfusion, RTM Light,RTM Heavy
Applications Lantor Soric XF
■ Marine:hulls,decks and structures of boats and yachts
■ Transportation:parts and panels ofcars,trailers, trucks and RV’s
■ Mass transit:interior and exterior oftrains,light rail and buses
■ Leisure:kayaks,surfboards,pools and tubs
■ Industrial:cladding panels,fans,containers and tanks
■ Wind Energy:nacelle covers and spinners
Dimensional data
| Properties | XF 1.5 | XF 2 | XF 3 | XF 4 | XF 5 | XF 6 | XF 10 | |
| Thickness mm | 1,5 | 2,0 | 3,0 | 4,0 | 5,0 | 6,0 | 10,0 | |
| Thicknessloss at 0,8bar | % | <10 | <10 | <10 | <10 | <10 | <10 | <10 |
| Rollength m | 100 | 80 | 50 | 40 | 30 | 25 | 15 | |
| Roll width m | 1,27 | 1,27 | 1,27 | 1,27 | 1,27 | 1,27 | 1,27 | |
| Maxprocessing temperature ℃ | 170 | 170 | 170 | 170 | 170 | 170 | 170 | |
| Dry weight g/m² | 100 | 135 | 180 | 250 | 320 | 345 | 625 | |
| Resin uptake kg/m² | 1,0 | 1,0 | 1,4 | 1,9 | 2,4 | 2,8 | 5,4 | |
| Densityimpregnated kg/m³ | 650 | 600 | 600 | 600 | 600 | 600 | 600 | |
Typical mechanical properties of Lantor Soric
impregnated with unsaturated polyester resin
| Mechanical properties | unit | value | fest method |
| Flexural strength | MPa | 8 | ASTM D790 |
| Flexural modules | MPa | 800 | ASTM D790 |
| Tensile strengthacross layers | MPa | 4 | ASTM C297 |
| Compression strength:10%strain | MPa | 8 | ISO 844 |
| Shear strength | MPa | 3.5 | ASTM C273-61 |
| Shear modules | MPa | 35 | ASTM C273-61 |